ABSTRACT The electromagnetic properties of Carbon-Graphene Xerogel (CGX), Flaky graphite (GR) and Nickel-Zinc ferrite (FeNiZn) composites in polystyrene (PS) matrix were studied in the X-Band range (8.2 – 12.4 GHz). In this work the Expanded Polystyrene (EPS) waste material was processed into polystyrene through the recycling of EPS. The polystyrene obtained was utilized as dielectric matrix, mainly because PS is a well-known organic polymer that presents low dielectric loss and light weight, which contribute to applications in composites for the aerospace field. In order to produce the final composite specimens, the CGX additive was previously synthesized through a sustainable method that employed the use of waste from the paper and pulp industry (black liquor). Afterwards, the morphological and structural analysis were made through Scanning Electron Microscope (SEM) and Raman Spectrometer, respectively. On the other hand, the magnetic ferrite material, FeNiZn, was obtained for the composite production through calcination, whereas the GR utilized was commercially obtained. It was observed that the increase of CGX and GR influenced on the increase of the Complex Permittivity, and that 10 wt% CGX + 50wt% FeNiZn composite sample demonstrated an absorption peak at 10.5 GHz. The results are relevant concerning the recycling of EPS waste through its use as dielectric matrix, thus developing greener and low-weight composite materials to be used in microwave applications.

In this manuscript, the electromagnetic wave absorption properties of sustainable porous carbon composites were evaluated over the X-band frequency range (8.2 - 12.4 GHz). The porous carbon material was made from the byproduct of cellulose production and was used as additive on the development of radar absorbing material (RAM) composites. These porous carbon materials have different characteristics, such as porosity size (180 µm < Ø1 < 250 µm and 425 µm < Ø2 < 500 µm) and particle size (ϕ1 < 250 µm and 250 µm < ϕ2 < 425 µm). Composite materials were also studied as frequency selective surface (FSS) structures. It was shown how complex permittivity and reflection loss (RL) can be manipulated over the frequency range using FSS structure. While regular RAM presented RL of 19 dB at ~11.8 GHz, FSS structure presented a RL of 19 dB shifted to 12.4 GHz regarding the same carbon porous material (with particles between 250 and 425 µm and porosity between 180 and 250 µm). It was demonstrated here the potential use of sustainable porous carbon as RAM, and how FSS structure can be used to tune the frequency of the RL maximum peak.